Fabrication and Enzymatic Disorganization of Multiresponse Worm-Like Micelles

How to fabricate multiresponse worm-like micelles (WLMs) and the corresponding green disposal is still challenging. A strategy of fabricating the surfactant-based WLMs that can respond simultaneously to light, heat, and pH was developed by using triple-response sodium (E)-2-(4-(phenyldiazenyl)phenoxy) acetate (AzoNa) and butyrylcholinesterase (BChE)-hydrolyzable palmitoylcholine bromide (PCB). Under the optimal molar ratio of AzoNa to PCB (∼0.5), the PCB-AzoNa WLMs formed with a maximum zero-shear viscosity (η₀) value of about 2.1 × 10⁵ mPa·s and an average diameter (D) of 4.1 ± 0.6 nm under conditions of 37 °C and pH 7.4. After irradiated with 365 nm UV light for 80 min, AzoNa underwent the trans-to-cis transition, by which the PCB-AzoNa WLMs was destroyed; however, the PCB-AzoNa WLMs could be reformed upon the irradiation of 455 nm blue light for 18 h or heating at 70 °C for 45 min due to the cis-to-trans isomerization of AzoNa. When pH changed from 7.4 to 2.0, the PCB-AzoNa WLMs was destroyed rapidly because of the conversion of AzoNa to the acid form of AzoH, whereas the PCB-AzoNa WLMs could be reformed after pH was restored to 7.4. The multiple responsiveness of the PCB-AzoNa WLMs was reversible due to the reversible trans-cis isomerization or protonation of AzoNa. Besides, the average D values of light, heat, and pH-regenerated PCB-AzoNa WLMs were 4.2 ± 0.7, 4.0 ± 0.7, and 4.0 ± 0.6 nm, respectively. Finally, the PCB-AzoNa WLMs could be enzymatically disorganized under conditions of 37 °C and pH 7.4 due to the BChE-catalyzed hydrolysis of PCB. We hope that the fabrication and enzymatic disorganization strategies for PCB-based multiresponse WLMs presented here will find potential applications in the formulation of antimicrobial household and personal care products containing PCB and in the green disposal of viscous waste containing PCB.