Tooth-composite bond failure with a universal and an etch-and-rinse adhesive depending on mode and frequency of...

To evaluate the effect of an additional layer of universal adhesive on the interfacial enamel/dentin-composite gap formation in relation to application mode and aging, via spectral domain optical coherence tomography (SD-OCT) and scanning electron microscopy (SEM).

In vitro class V cavities in 114 caries-free premolars were restored by applying one or two layers of a universal adhesive (Scotchbond Universal, SBU) in self-etch (se) and etch-and-rinse (er) mode or the reference adhesive OptiBond FL (OFL-er). The restorations were imaged by SD-OCT (six groups, n = 8) and SEM (n = 3) directly after filling (t1), water storage (t2, 24 h), embedding (t3), and thermo-mechanical loading (t4, TCML). The interfacial gaps were quantified using 26 parameters and analyzed using principal component analysis and linear mixed effect models.

Gap formation at enamel and dentin was significantly influenced by the adhesive, the application mode and number of layers (p < 0.001). This was due to the influence of the SBU-er mode (p < 1e-05), which showed significantly more gap formation and a greater range of variation with double application when compared to SBU-se and OFL. The fewest interfacial gaps occurred with one or two applications of OFL-er and one layer of SBU-er.

Adhesive application mode and the number of adhesive layers are relevant factors in the tooth-composite bond failure. Double application worsened the adaptation of SBU to freshly prepared dentin conditioned with phosphoric acid.