Magnetically separable Pd-iron-oxides composites as highly efficient and recyclable catalysts for ultra-rapid...

When precious nano-metals are used as environmental catalysts, it is important to tune the particle sizes and the reusability of the nano-metals for achieving their highly efficient catalytic performance at a low cost. In the present work, magnetic iron oxides (FeO_x-Y) nanoparticles were pre-prepared as supports of nano-metals, where Y represented the mole percentage of Fe(III) in the total iron (Y ≥ 50 %). FeO_x-Y (support), PdCl₄^2- (Pd source) and NaBH₄ (reducing agent) were added into the organic pollutant solution containing 2,2',4,4'-tetrabromodiphenyl ether (BDE47). After the NaBH₄ was added, the followed reaction realized not only the rapid in-situ preparation of a Pd-loaded FeO_x-Y composite catalyst (Pd-FeO_x-Y), but also the ultra-fast and complete debromination of BDE47 within 30 s. Comparing the case without adding FeO_x-Y, the debromination efficiency of BDE47 was much promoted in the presence of FeO_x-Y. The support-induced enhancing effect on the catalytic ability of Pd nanoparticles was improved by increasing the Fe(III) content in the support, being attributed to the much more hydroxyl groups on the support surface. Considering both the catalytic and recovery abilities of Pd-FeO_x-Y, Pd-FeO_x-75 was the optimal choice because it could be magnetically recovered and re-used for multiple cycles with high catalytic activities. The presently developed "catalyst preparation-pollutant degradation" one-pot system could be applied to conduct complete debromination of all the PBDEs.