Engineering Multinanochannel Polymer-Intercalated Graphene Oxide Membrane for Strict Volatile Sieving in Membrane...

Graphene oxide (GO) membranes enabled by subnanosized diffusion channels are promising to separate small species in membrane distillation (MD). However, the challenge of effectively excluding small volatiles in MD persists due to the severe swelling and subsequent increase in GO interlamination spacing upon direct contact with the hot feed. To address this issue, we implemented a design in which a polymer is confined between the GO interlaminations, creating predominantly 2D nanochannels centered around 0.57 nm with an average membrane pore size of 0.30 nm. Compared to the virginal GO membrane, the polymer-intercalated GO membrane exhibits superior antiswelling performance, particularly at a high feed temperature of 60 °C. Remarkably, the modified membrane exhibited a high flux of approximately 52 L m^-2 h^-1 and rejection rates of about 100% for small ions and 98% for volatile phenol, with a temperature difference of 40 °C. Molecular dynamics simulations suggest that the sieving mechanisms for ions and volatiles are facilitated by the narrowed nanochannels within the polymer network situated between the 2D nanochannels of GO interlaminations. Concurrently, the unrestricted permeation of water molecules through the multinanochannel GO membrane encourages high-flux desalination of complex hypersaline wastewater.