Simultaneously Enhanced Thermoelectric and Mechanical Performance in SnSe-Based Nanocomposites Produced via Sintering...

Both thermoelectric and mechanical properties are important to the practical applications of thermoelectric materials. Herein, we develop a strategy for alloying KCu₇S₄ to improve the dimensionless figure of merit (zT), compressive strength, and Vickers hardness of polycrystalline SnSe. Through chemical synthesis and particle mixing in solutions, powders with SnSe nanoparticles and KCu₇S₄ nanowires are produced, and the subsequent spark plasma sintering triggers the reaction between the two chalcogenides, resulting in the formation of Cu₂SnSe₃ nanoparticles and substitution of Cu and S in the SnSe matrix. The composition tuning and secondary phase formation effectively enhance the power factor and diminish the lattice thermal conductivity, leading to a maximum zT of 1.13 at 823 K for the optimal sample, which is improved by 135% over that of SnSe. Simultaneously, the compressive strength and hardness are also enhanced, as exemplified by a high compressive strength of 135 MPa that is enhanced by ∼81% compared to that of SnSe. The current study demonstrates effective composite and composition design toward enhanced thermoelectric and mechanical performance in polycrystalline SnSe.