Antibacterial effect of Ag-containing hydroxyapatite thin film fabricated by sputtering

Infections related to joint prosthesis are still a major concern for orthopedic surgeons. Hydroxyapatite (HA) is a useful biocompatible material because of its good osteocompatibility. Antibacterial HA coatings have been fabricated with addition of antibacterial agents such as Ag to HA using the plasma spraying method. However, the plasma-sprayed HA coating suffers from fractures at large thicknesses. The sputter-coated HA thin film has a high density, and has been applied clinically for dental implants. However, there are no extensive studies on Ag-containing HA thin films.

The aim of this study was to prepare an Ag-containing HA thin film by sputtering, and evaluate its antibacterial effect and cytotoxicity.

The Ag-containing HA thin films were prepared by radio-frequency magnetron sputtering. The films were characterized using X-ray photoelectron spectroscopy, X-ray diffractometry, and scanning electron microscopy (SEM). The antibacterial activities and cytotoxicities of the films were also evaluated.

The Ag/Ca molar ratio of the films increased with the Ag ratio in the target. The SEM observation of the hydrothermally treated films showed surfaces covered with globular particles. All Ag-containing HA films exhibited an antibacterial effect against E. Coli. The number of cells of the films decreased with the Ag ratio. The films subjected to the hydrothermal treatment exhibited a higher number of cells than the as-sputtered films.

The Ag-containing HA thin film was effective in terms of antibacterial effect, and had a low cytotoxicity in the proliferation of osteoblast cells at a low Ag ratio in the target.