Mechanistic and Kinetic Measurements of Elementary Surface Reactions Using Temperature-Programmed X-ray Photoelectron...

This paper describes a method by which surface-reaction kinetics can be measured by slowly and precisely ramping up the surface temperature at a constant rate while simultaneously collecting X-ray photoelectron spectra (XPS). This approach results in the collection of a large amount of data over relatively small temperature steps to produce quasi-continuous kinetic data. The method is illustrated for the desorption and reaction of diethyl disulfide (DEDS) on a Au(111) substrate in ultrahigh vacuum, where the results can be compared with previous conventional temperature-programmed desorption (TPD) data from Au(111). Experiments were carried out using a double-pass cylindrical-mirror analyzer with a channeltron detector to demonstrate how this approach can be implemented in a routine, multitechnique vacuum chamber. The approach will be even more effective in a more modern, specialized XPS apparatus with high-transmission hemispherical analyzers with multichannel array detectors, which will enable the spectra of several elements to be measured simultaneously. The results yielded an activation energy for multilayer desorption of DEDS of 41 ± 1 kJ/mol, with a pre-exponential factor of 8 ± 7 × 10¹² s^-1, an activation energy of 53 ± 6 kJ/mol and pre-exponential factor of 9 ± 8 × 10¹³ s^-1 for monolayer desorption and an activation energy of 90 ± 6 kJ/mol with a prefactor of 1.0 ± 0.3 × 10¹⁵ s^-1 for the reaction of adsorbed ethyl thiolate species to adsorbed DEDS. While these results were collected for a system for which the kinetic data could have been obtained using conventional TPD, this method can be more usefully applied to those surface reaction processes that do not rely on the formation of desorption products. This system, having been previously studied by TPD, facilitates a comparison with results obtained by conventional methods.