One-pot solvothermal preparation of the porous NiS2//MoS2 composite catalyst with enhanced low-temperature
Kun Sun1, Hailing Guo1, Chao Feng2
1State Key Laboratory of Heavy Oil Processing, Key Laboratory of Catalysis, China National Petroleum Corp. (CNPC), China University of Petroleum (East China), Qingdao 266555, China.
Abstract:
The simple preparation of mesoporous NiS2//MoS2 composite catalyst through a one-pot solvothermal method is presented. The improvement of the specific surface area (220 m2/g) and the construction of the porous structure are realized by this method in the case of no support. The organics acts as a microscopic binder contribute to uniform stacking of MoS2 with NiS2 clusters. The composite structure including NiS2 and MoS2 was obtained (proved by XRD, XPS, TEM, IR, UV-vis and RAMAN) and changed the microelectronic environment of the active metal surface (DFT calculation). The mesoporous NiS2//MoS2 catalyst (Ni1Mo1-200) showed an excellent hydrodesulfurization performance of dibenzothiophene (DBT conversion: 78 % at 260 °C) and a high ratio of direct desulfurization pathway (SDDS/HYD = 16.6) at a low reaction temperature. By combining the characterization and theoretical calculation results, the advantages of this NiS2//MoS2 composite structure in synergistic catalysis was further confirmed.
More Related Videos
10:57Synthesis and Performance Characterizations of Transition Metal Single Atom Catalyst for Electrochemical CO2 Reduction
Published on: April 10, 2018
08:13Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area
Published on: February 19, 2018