The flexural strength of 3D-printed provisional restorations fabricated with different resins: a systematic review
Ravinder S Saini1, Vishwanath Gurumurthy1, Syed Altafuddin Quadri1
1Department of Dental Technology, COAMS, King Khalid University, Abha, Saudi Arabia.
Background:
Three-dimensional (3D) printing technology has revolutionized dentistry, particularly in fabricating provisional restorations. This systematic review and meta-analysis aimed to thoroughly evaluate the flexural strength of provisional restorations produced using 3D printing while considering the impact of different resin materials.
Methods:
A systematic search was conducted across major databases (ScienceDirect, PubMed, Web of Sciences, Google Scholar, and Scopus) to identify relevant studies published to date. The inclusion criteria included studies evaluating the flexural strength of 3D-printed provisional restorations using different resins. Data extraction and quality assessment were performed using the CONSORT scale, and a meta-analysis was conducted using RevMan 5.4 to pool results.
Results:
Of the 1914 initially identified research articles, only 13, published between January 2016 and November 2023, were included after screening. Notably, Digital Light Processing (DLP) has emerged as the predominant 3D printing technique, while stereolithography (SLA), Fused Deposition Modeling (FDM), and mono-liquid crystal displays (LCD) have also been recognized. Various printed resins have been utilized in different techniques, including acrylic, composite resins, and methacrylate oligomer-based materials. Regarding flexural strength, polymerization played a pivotal role for resins used in 3D or conventional/milled resins, revealing significant variations in the study. For instance, SLA-3D and DLP Acrylate photopolymers displayed distinct strengths, along with DLP bisacrylic, milled PMMA, and conventional PMMA. The subsequent meta-analysis indicated a significant difference in flexure strength, with a pooled Mean Difference (MD) of - 1.25 (95% CI - 16.98 - 14.47; P < 0.00001) and a high I2 value of 99%, highlighting substantial heterogeneity among the studies.
Conclusions:
This study provides a comprehensive overview of the flexural strength of 3D-printed provisional restorations fabricated using different resins. However, further research is recommended to explore additional factors influencing flexural strength and refine the recommendations for enhancing the performance of 3D-printed provisional restorations in clinical applications.