Superhydrophilic and Underwater Superoleophobic Copper Mesh Coated with Bamboo Cellulose Hydrogel for Efficient...

Super-wetting interface materials have shown great potential for applications in oil-water separation. Hydrogel-based materials, in particular, have been extensively studied for separating water from oily wastewater due to their unique hydrophilicity and excellent anti-oil effect. In this study, a superhydrophilic and underwater superoleophobic bamboo cellulose hydrogel-coated mesh was fabricated using a feasible and eco-friendly dip-coating method. The process involved dissolving bamboo cellulose in a green alkaline/urea aqueous solvent system, followed by regeneration in ethanol solvent, without the addition of surface modifiers. The resulting membrane exhibited excellent special wettability, with superhydrophilicity and underwater superoleophobicity, enabling oil-water separation through a gravity-driven "water-removing" mode. The super-wetting composite membrane demonstrated a high separation efficiency of higher than 98% and a permeate flux of up to 9168 L·m^-2·h^-1 for numerous oil/water mixtures. It also maintained a separation efficiency of >95% even after 10 cycles of separation, indicating its long-term stability. This study presents a green, simple, cost-effective, and environmentally friendly approach for fabricating superhydrophilic surfaces to achieve oil-water separation. It also highlights the potential of bamboo-based materials in the field of oil-water separation.