One-Dimensional La_0.2Sr_0.8Cu_0.4Co_0.6O_3-δ Nanostructures for Efficient Oxygen Evolution Reaction

Producing oxygen and hydrogen via the electrolysis of water has the advantages of a simple operation, high efficiency, and environmental friendliness, making it the most promising hydrogen production method. In this study, La_0.2Sr_0.8Cu_0.4Co_0.6O_3-δ (LSCC) nanofibers were prepared by electrospinning to utilize non-noble perovskite oxides instead of noble metal catalysts for the oxygen evolution reaction, and the performance and electrochemical properties of LSCC nanofibers synthesized at different firing temperatures were evaluated. In an alkaline environment (pH = 14, 6 M KOH), the nanofibers calcined at 650 °C showed an overpotential of 209 mV at a current density of 10 mA cm^-2 as well as good long-term stability. Therefore, the prepared LSCC-650 NF catalyst shows excellent potential for electrocatalytic oxygen evolution.