Efficiency and Mechanism of Surface Reinforcement for Recycled Coarse Aggregates via Magnesium Phosphate Cement

Recycled aggregate concrete (RAC) exhibits inferior mechanical and durability properties owing to the deterioration of the recycled coarse aggregate (RCA) surface quality. To improve the surface properties of RCA, the reinforcement efficiency of RAC, and the maneuverability of the surface treatment method, this study used magnesium phosphate cement (MPC), a clinker-free low-carbon cement with excellent bonding properties, to precoat RCA under three-day pre-conditioning. Moreover, variable amounts of fly ash (FA) or granulated blast furnace slag (GBFS) were utilized to partly substitute MPC to enhance the compressive strength and chloride ion penetration resistance. Subsequently, FA-MPC and GBFS-MPC hybrid slurries with the best comprehensive performance were selected to coat the RCA for optimal reinforcement. The crushing value and water absorption of RCA, as well as the mechanical strengths and durability of RAC, were investigated, and microstructures around interfaces were studied via BSE-EDS and microhardness analysis to reveal the strengthening mechanism. The results indicated that the comprehensive property of strengthening paste was enhanced significantly through substituting MPC with 10% FA or GBFS. Surface coating resulted in a maximum reduction of 8.15% in the crushing value, while the water absorption barely changed. In addition, modified RAC outperformed untreated RAC regarding compressive strength, splitting tensile strength, and chloride ion penetration resistance with maximum optimization efficiencies of 31.58%, 49.75%, and 43.11%, respectively. It was also evidenced that the improved MPC paste properties enhanced the performance of modified RAC. Microanalysis revealed that MPC pastes exhibited an excellent bond with RCA or new mortar, and the newly formed interfacial transition zone between MPC and the fresh mortar exhibited a dense microstructure and outstanding micro-mechanical properties supported with an increase in the average microhardness value of 30.2-33.4%. Therefore, MPC pastes incorporating an appropriate mineral admixture have enormous potential to be utilized as effective RCA surface treatment materials and improve the operability of RCA application in practice.