Nondestructive Evaluation of Tensile Stress-loaded GFRPs Using the Magnetic Recording Method

This paper presents the results of inspecting tensile stress-loaded GFRP (glass fiber-reinforced polymer) samples using the Magnetic Recording Method (MRM). The MRM can be utilized solely to examine ferromagnetic materials. The modification was proposed in order to examine nonmagnetic composites. Ferromagnetic strips made of low-carbon steel DC01 were bonded to the surface using an adhesive composed of epoxy resin with the addition of triethylenetetramine. The modified method's feasibility was tested on six samples made of GFRP. The research procedure consisted of three steps. In the first step, a metal strip is glued at the top surface of each sample, and an array of 100 cylindrical permanent magnets is used to record a sinusoidal magnetic pattern on the strip. The initial residual magnetization is measured in the second step, and the samples are subjected to static stress. In the third step, the residual magnetization is measured one more time. Ultimately, the measurement results from the second and third steps are compared. Generally, the applied stress causes changes in the amplitude and frequency of the sinusoidal magnetization pattern. In the case of GFRP, the frequency changes have not been used for evaluation due to minimal variations. The statistical parameters (mean, median, max, and mode) of the RMS (root mean square) value of the sinusoidal pattern were calculated and analyzed. The analysis demonstrates that the modified method is suitable for providing unequivocal and exact information on the load applied to a nonmagnetic composite material. For the presented results, the applied load can be assessed unambiguously for the samples elongated up to 0.6%.