Microwave disinfection of facial silicone prostheses, part 2: Mechanical properties
Penchanok Santhaveesuk1, Pravej Serichetaphongse2, Sudarat Kiat-Amnuay3
1Former Prosthodontic Resident, Department of Prosthodontics, Faculty of Dentistry, Chulalongkorn University, Bangkok, Thailand; and Former AEGD Preceptor, University of Texas Health Science Center at Houston, School of Dentistry, Houston, Texas.
Statement Of Problem:
Part 1 of this 2-part study determined that microwave disinfection did not degrade the color stability of facial silicone prostheses. However, investigations on the effects of microwave disinfection on the mechanical properties of different silicone elastomers are lacking.
Purpose:
The purpose of this in vitro study was to examine the mechanical properties of commonly used colored facial silicone elastomers before and after microwave disinfection over a simulated 1.5-year period.
Material And Methods:
Six commonly used facial silicone elastomers: MDX4-4210, MDX4-4210/Type A, M511, A-2186, VST-50, and A-2000 were combined with functional intrinsic silicone pigments and opacifier (red, yellow, blue, and white). A total of 288 specimens were fabricated (n=12). Half of the specimens were tested for mechanical properties as the baseline, while the other specimens were tested after microwave disinfection. Microwave disinfection was performed with 660 W, 6 minutes of exposure time, and microwaved for 18 cycles to simulate 1.5 years of usage (one 6-minute exposure monthly). For mechanical property testing, all specimens were tested for tensile strength and percentage elongation (ASTM D412), tear strength (ASTM D624), and hardness (ASTM D2240). For each property, a 2-way ANOVA (silicone type and microwave disinfection factors) and Tukey multiple comparison test were performed using the R statistical software program (α=.05).
Results:
Following microwave disinfection, tensile strength and percentage elongation of A-2000 increased significantly (P<.05). MDX4-4210, MDX4-4210/Type A, and A-2000 showed significant increases in their hardness (P<.001). Tear strength also increased significantly for MDX4-4210 and VST-50 (P<.05). Among the materials tested (ranked from highest to lowest value,=not statistically significant different), for tensile strength, VST-50>A-2186=A-2000>MDX4-4210/Type A=M511=MDX4-4210 (P<.05). For percentage elongation, VST-50>MDX4-4210/Type A>A-2186>M511=A-2000=MDX4-4210=M511 (P<.05). For hardness, A-2000=A-2186>M511=VST-50>MDX4-4210>MDX4-4210/Type A (P<.05). For tear strength, VST-50>A-2186>A-2000>M511>MDX4-4210/Type A=MDX4-4210 (P<.05).
Conclusions:
Overall, the mechanical properties of all the silicones tested were not adversely affected by microwave disinfection. VST-50 showed the best mechanical properties among the materials tested both before and after microwave disinfection. Microwave energy is a safe method of disinfecting the silicone elastomers tested in this study.