Study on the dynamic adsorption and recycling of phosphorus by Fe-Mn oxide/mulberry branch biochar composite
Liang Meina1,2, Mushi Qiao1, Qing Zhang3
1School of Envormental Science and Engneering, Guilin Unversity of Technology, Guilin, 541004, People's Republic of China.
Abstract:
In this study, the Fe-Mn oxide/mulberry stem biochar composite adsorbent (FM-MBC) was prepared and fully characterized by SEM-EDS, XRD, BET, and XPS. The solution pH (3.0, 4.5, and 6.0), initial concentration of phosphorus (10, 20, and 30 mg L-1), adsorbent bed height (2, 3, and 4 cm), and solution flow rate (1, 2, and 3 mL min-1) were investigated to analyze the breakthrough curves. The results showed that the breakthrough time was shortened as the initial phosphorus concentration, the flow rate increased and the bed height decreased. Higher initial phosphorus concentrations, flow rates, and lower bed heights, led to a faster breakthrough of phosphate ions in the FM-MBC adsorbent. Additionally, it was observed that increasing the pH value was not conducive to the adsorption of phosphorus by the FM-MBC adsorbent. Dynamic adsorption data were fitted to four models (Yoon-Nelson, Thomas, Adams-Bohart, and Bed Depth Service Time), and the R2 values of the Thomas and Yoon-Nelson models exhibited minimal variation, suggesting that the dynamic adsorption process of FM-MBC was rather intricate. The saturated fixed-bed column (including FM-MBC) was regenerated with NaOH or HCl, and it was found that a 0.1 mol L-1 NaOH solution had the best regeneration effect. XRD analysis showed that the reaction product between the FM-MBC composite and phosphate anions was Fe3(PO4)2·H2O. Moreover, the experimental results that FM-MBC can successfully be used to remove phosphorus from actual wastewater.