Construction of 3D network aluminum sludge-based hydrogel beads: combination of macroization, amino...

An aluminum sludge-based composite material was constructed against the problems of phosphorus pollution and the waste of aluminum sludge resources. Utilizing metal Ce doping and hydrogel microbeads with pore preparation, the adsorption performance of the original sludge was improved. Meanwhile, the macroscopic body was constructed, and on this basis, polyethyleneimine (PEI) was introduced to complete the amino functionalization further to enhance the adsorption of phosphorus by the adsorbent, and NH-CeAIS-10 microbeads were successfully prepared. In adsorption, microbeads with larger specific surface area and richer functional groups are better choice compared to original sludge. The results of SEM, BET, FT-IR, and XPS analyses indicate that the adsorption of phosphorus by the microbeads is mainly achieved through electrostatic interactions, ligand exchange, and the formation of inner-sphere complexes. According to the Langmuir model, the maximum phosphorus adsorption capacity of NH-CeAIS-10 was 29.56 mg g^-1, which was four times higher compared to native aluminum sludge. This also confirms the significant enhancement of phosphorus adsorption through the modification of aluminum sludge. Besides, in dynamic adsorption column experiments, the material exhibited up to 99% removal in simulated wastewater for up to 30 days, demonstrating the great adsorption potential of NH-CeAIS-10 in engineering applications.