Introducing gradient Er ions and oxygen defects into SrCoO3 for regulating structural, electrical and magnetic
Hongyuan Song1, Xuesong Wang1, Haorong Wu1
1Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming, 650093, PR China. yulan000@hotmail.com.
Abstract:
The SrCoO3- system has broad application potential due to its diverse crystal structures, oxidation stoichiometric ratio, and significant electrical and magnetic properties. However, it faces the challenges of a complex crystal structure and oxygen defect control in this material system. Herein, we introduce oxygen defects into SrCoO3-via Er doping to regulate the structural, electrical and magnetic transport properties. Sr1-ErCoO3- (x = 0-0.25) undergoes an evolution of structure and oxygen content (measured using the iodometric method) from hexagonal SrCoO2.626 (H + Co3O4) to cubic perovskite Sr0.9Er0.1CoO2.689 (CP) and finally to ordered tetragonal Sr0.8Er0.2CoO2.635 (OT). Among the three phases, Sr0.9Er0.1CoO2.689 (CP) exhibits the lowest resistivity, only 4.06 mΩ cm at room temperature, which is attributed to its high three-dimensional symmetry, overlap of O 2p and Co 3d orbitals at high oxygen ion concentration. Further introduction of Er ions and oxygen defects promotes the transformation from low spin Co4+ (LS, t52ge0g, S = 1/2) to high spin Co3+ (HS, t42ge2g, S = 2), and from the CoO6 octahedron (low magnetic moment transformation) to the CoO4.25 tetrahedron (high magnetic moment). The oxygen-deficient CoO4.25 layer appears, which can enhance the ordering of A sites and oxygen vacancies, and the CP phase transforms into room-temperature ferromagnetic Sr0.8Er0.2CoO2.635 (OT, TC∼330 K). Er ions provide unpaired electrons in the 2f orbital, which results in a strong magnetization of Sr0.8Er0.2CoO2.635 (OT, 4.66 μB/Co) at low temperatures.
More Related Videos
11:07Synthesis of Non-uniformly Pr-doped SrTiO3 Ceramics and Their Thermoelectric Properties
Published on: August 15, 2015
06:49Radio Frequency Magnetron Sputtering of GdBa2Cu3O7âˆ'ÃŽ ´/ La0.67Sr0.33MnO3 Quasi-bilayer Films on SrTiO3 STO Single-crystal Substrates
Published on: April 12, 2019
Related Concept Videos
01:26What is an Electrochemical Gradient?
The chemical gradient relies on differences in the abundance of a substance on the outside versus the inside of a cell and flows from areas of high to low ion concentration. In contrast, the electrical gradient revolves around an...
01:31Ferromagnetism
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human...
01:27Biasing of Metal-Semiconductor Junctions
In Schottky junctions, where the semiconductor is n-type, applying a positive voltage to the metal relative to the semiconductor reduces its Fermi...
02:58Properties of Transition Metals
02:54Molecular and Ionic Solids
Molecular Solids
Molecular crystalline solids, such as ice, sucrose (table sugar), and iodine, are solids that are composed of neutral molecules as their constituent units. These molecules are held together by weak intermolecular forces such as London dispersion forces, dipole-dipole interactions, or hydrogen bonds, which...