CAD-CAM resin composites: Effective components for further development
Satoshi Yamaguchi1, Hefei Li1, Takahiko Sakai2
1Department of Dental Biomaterials, Osaka University Graduate School of Dentistry, 1-8 Yamadaoka, Suita, Osaka 565-0871, Japan.
Objective:
This paper summarizes the effective components of computer-aided design and computer-aided manufacturing (CAD-CAM) resin composites that contribute to achieving greater mechanical properties and further development.
Methods:
In silico multi-scale analysis, in silico nonlinear dynamic finite element analysis (FEA), and artificial intelligence (AI) were used to explore the effective components of CAD-CAM resin composites. The effects of the filler diameter and silane coupling ratio on the mechanical properties of CAD-CAM resin composites have been clarified through multi-scale analysis. The effects of the filler contents, and filler and monomer compositions have been investigated by AI algorithms. The fracture behavior of CAD-CAM composite crown was analyzed using in silico non-linear dynamic FEA. The longevity of CAD-CAM composite crown was assessed through step-stress accelerating life testing (SSALT).
Results:
As the filler diameter decreases, there is an increase in elastic moduli and compressive strengths at the macroscale. At the nanoscale, a decrease in the filler diameter results in a decrease in the maximum value of the maximum principal strain. When the silane coupling ratio decreases, there is a decrease in the elastic modulus and compressive strength. According to the exhaustive search and feature importance analysis based on the AI algorithm, the combination of certain components was narrowed down to achieve a flexural strength of 269.5 MPa. The in silico non-linear FEA successfully detected the sign of the initial crack of the CAD-CAM composite molar crown. The SSALT revealed that CAD-CAM resin composite molar crowns containing nanofillers with a high fraction of resin matrix demonstrated great longevity.
Significance:
This paper summarized the effective components of CAD-CAM resin composites for their further development. The integration of in vitro and in silico approaches will expedite the advancement of CAD-CAM resin composites, offering benefits such as time efficiency and reduction of material waste for researchers and manufacturers.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
03:02Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins
Published on: January 17, 2025