Robust and self-lubricating polyvinyl alcohol tubes with a mucosa-like hierarchical architecture for endotracheal...

Mechanical mismatch between interventional intubation tubes and human tissues often triggers inevitable friction and causes secondary injury to patients during interventional therapy. Herein, we propose a fabrication strategy of a self-lubricating polyvinyl alcohol (PVA) tube by industrial extrusion technology followed by simple infiltration with water. First, biocompatible glycerin was introduced to weaken the intrinsic hydrogen interaction of PVA by new molecular complexation, broadening the gap between the melting and decomposition temperatures and enabling the stable extrusion of the PVA tube. Subsequently, the as-prepared PVA tube was infiltrated with an aqueous solution to construct a strong hydrogen bonding network between PVA and water molecules, forming a soft hydration layer similar to the upper epithelium layer of mucosa. Benefiting from the solid and liquid properties of the hydration layer as well as the small proportion relative to the whole, the infiltrated PVA tube exhibited excellent hydration lubrication behavior and robust mechanical property. The friction coefficient, tensile strength and elongation at break were measured to be 0.05, 26.2 MPa and 654%, respectively, surpassing the values of 0.5, 16.4 MPa and 240% observed in a commercial polyvinyl chloride tube. In vitro, the PVA intubation tube demonstrated significant biocompatibility, and short-term exposure exhibited minimal impacts on the morphology and proliferation of L929 cells. Ultimately, the potential of the infiltrated PVA tube for interventional intubation was demonstrated successfully using an in vivo rabbit model, providing a new idea for the follow-up development of interventional intubation tubes.