Chemical Synthesis of Porous Barium Titanate Thin Film and Thermal Stabilization of Ferroelectric Phase by Porosity-Induced Strain
Published on: March 27, 2018
Ultra-high resistive switching current ratio and improved ferroelectricity and dielectric tunability performance in a
Xi Zhang1,2, Xin Chen2, J P Cao1,2
1School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China. J.miao@ustb.edu.cn.
Abstract:
A BaTiO3/SrCoO2.5 (BTO/SCO) bilayer and a BTO single film were prepared by radio frequency magnetron sputtering on La0.7Sr0.3MnO3 (LSMO) buffered SrTiO3 (001) substrates. Interestingly, compared with reported BTO-based films, the BTO/SCO/LSMO heterostructure has a maximum ON/OFF current ratio of ∼945. More interestingly, compared with the BTO single layer, a larger Pr (∼18.4 μC cm-2) and larger dielectric tunability (∼71.9%) were achieved in the BTO/SCO bilayer. The improved performance may be attributed to the large tetragonality and improved oxygen vacancy concentrations in the BTO/SCO/LSMO heterostructure. Furthermore, our BTO/SCO/LSMO stacks exhibit potential for flexible electronic informational devices.
More Related Videos
06:49Radio Frequency Magnetron Sputtering of GdBa2Cu3O7âˆ'ÃŽ ´/ La0.67Sr0.33MnO3 Quasi-bilayer Films on SrTiO3 STO Single-crystal Substrates
Published on: April 12, 2019
06:44Tuning Oxide Properties by Oxygen Vacancy Control During Growth and Annealing
Published on: June 9, 2023