Fabrication, characterization and release behavior of α-tocopherol acetate-loaded pH-responsive...

Microbeads are used in personal care and cosmetic products (PCCPs) but are produced from nondegradable materials. Biodegradable polyhydroxybutyrate (PHB) has been recognized as a promising alternative material for use in PCCPs; however, utilizing PHB to encapsulate PCCPs is challenging because PCCPs need to be protected from the environment but their release needs to be permitted under specific physiological conditions. The aim of this work was to develop and evaluate pH-responsive cellulose acetate phthalate (CAP) to formulate lipophilic α-tocopherol acetate (α-TA)-loaded pH-responsive PHB/CAP microbeads. The influences of the PHB/CAP ratio and initial α-TA loading on the microbead size, surface morphology, encapsulation efficiency (%EE), loading capacity (%LC), and α-TA release profile were studied. The microbeads exhibited a spherical shape with a size of 328.7 ± 2.9 μm. The EE and LC were 86.7 ± 2.6 % and 13.5 ± 0.4 %, respectively. The release profile exhibited pH-responsive characteristics. These α-TA-loaded pH-responsive microbeads were stable with >50 % of the α-TA remaining after 90 days at 4, 25 and 45 °C in the dark. The results from the cytotoxicity assay with PSVK1 cells demonstrated that the microbeads were nontoxic. Hence, our developed formulation has the potential to be used to encapsulate oil-based drugs to formulate lipophilic substance-loaded pH-responsive microbeads.