Flame retardant, high mechanical strength, transparent and water-resistant epoxy composites modified with chitosan...

Adding bio-based flame retardants to improve the flame retardancy of polymer materials without sacrificing other properties is a great challenge. Herein, a novel flame-retardant CS-DOPA was prepared from chitosan and 10-hydroxy-9,10-dihydro-9-oza-10-phosphaphenanthrene-10-oxide by acid-base neutralization reaction and fully characterized. The 4 wt% CS-DOPA modified EP showed good flame retardancy in both gaseous and condensed phase. The peak heat release rate, total smoke production, CO production, and smoke production rate of EP composites containing 4 wt% CS-DOPA were reduced by 55 %, 34 %, 45 %, and 46 %, respectively, to pass the UL-94 V-1 rating with a limiting oxygen index of 34.1 %. The CS-DOPA contributes to the formation of the condensed phase of the thermo-oxidation-resistant high-quality char layer with non-flammable other and phosphorus-containing free radicals released in the gas phase. In addition, EP/4CS-DOPA has good water resistance, mechanical properties, and transparency, with tensile and flexural strength improved by 12.7 % and 13.9 %, respectively, and still has high strength even after water treatment. The present work provides a green and facile strategy to use chitosan as a main raw material to manufacture EP materials with high performance.