Tuning the Magnetic Behavior of Zinc Ferrite via Cobalt Substitution: A Structural Analysis

Cobalt-doped zinc ferrite is a contemporary material with significant structural and magnetic characteristics. Our study explores the magnetic properties of cobalt-substituted zinc ferrite (Zn_xCo_1-xFe₂O₄), synthesized via a simple sol-gel method. By varying the cobalt ratio from 0 to 0.5, we found that zinc substitution impacts both the magnetization and lattice parameters. FTIR analysis suggested the presence of functional groups, particularly depicting an M-O stretching band, within octahedral and tetrahedral clusters. X-ray diffraction analysis confirmed the phase purity and cubic structure. The synthesized materials exhibited an average particle size of 24-75 nm. Scanning electron microscopy revealed the morphological properties, confirming the formation of truncated octahedral particles. In order to determine the stability, mass loss (%), and thermal behavior, a thermal analysis (thermogravimetric analysis (TGA)/differential thermal analysis (DTA)) was performed. The magnetic properties of the synthesized ferrites were confirmed via a vibrating sample magnetometer (VSM). Finally, the highest saturated magnetization and lowest coercivity values were observed with higher concentrations of the cobalt dopant substituting zinc. The synthesized nanomaterials have good stability as compared to other such materials and can be used for magnetization in the near future.