Preparation of Bio-Based Polyurethane Coating from Citrullus colocynthis Seed Oil: Characterization and Corrosion...

In this study, a new epoxidized oil from Citrullus colocynthis seed oil (CCSO) was obtained for a potential application in the formulation of polyurethane coatings. Initially, the fatty acid composition of CCSO was determined by gas chromatography-mass spectrometry (GC-MS). Subsequently, the epoxidation of CCSO was performed with in situ generated peracetic acid, which was formed with hydrogen peroxide (30 wt.%) and glacial acetic acid and catalyzed with sulfuric acid. The reaction was continued at a molar ratio of 1.50:1.0 of hydrogen peroxide to double bond (H₂O₂:DB) for 6 h at a controlled temperature of 60 °C. The resulting epoxidized oil was then used to produce a bio-based polyol by hydroxylation. The molar ratio of epoxy groups to methanol and distilled water was maintained at 1:11:2, and the reaction was carried out for 2 h at a controlled temperature of 65 °C. The major functional groups of the epoxidized oil and its polyol were validated by Fourier-transform infrared (FT-IR) and proton nuclear magnetic resonance (¹H NMR) spectroscopies. A polyurethane (PU) coating was produced from the synthesized polyol and 3HDI isocyanurate, keeping the molar ratio of NCO:OH at 1:1. The resulting PU coating was then applied to glass and aluminum panels (Al 1001). After the film was cured, the properties of the PU coating were evaluated using various techniques including pencil hardness, pendulum hardness, adhesion, gloss, chemical resistance, and EIS tests. The results show that the PU coating obtained from CCSO is a promising new raw material for coating applications.