Light-enhanced oxygen degradation of MAPbBr₃ single crystal

Organometal halide perovskites are promising materials for optoelectronic applications, whose commercial realization depends critically on their stability under multiple environmental factors. In this study, a methylammonium lead bromide (MAPbBr₃) single crystal was cleaved and exposed to simultaneous oxygen and light illumination under ultrahigh vacuum (UHV). The exposure process was monitored using X-ray photoelectron spectroscopy (XPS) with precise control of the exposure time and oxygen pressure. It was found that the combination of oxygen and light accelerated the degradation of MAPbBr₃, which could not be viewed as a simple addition of that by oxygen-only and light-only exposures. The XPS spectra showed significant loss of carbon, bromine, and nitrogen at an oxygen exposure of 10¹⁰ Langmuir with light illumination, approximately 17 times of the additive effects of oxygen-only and light-only exposures. It was also found that the photoluminescence (PL) emission was much weakened by oxygen and light co-exposure, while previous reports had shown that PL was substantially enhanced by oxygen-only exposure. Measurements using a scanning electron microscope (SEM) and focused ion beam (FIB) demonstrated that the crystal surface was much roughened by the co-exposure. Density functional theory (DFT) calculations revealed the formation of superoxide and oxygen induced gap state, suggesting the creation of oxygen radicals by light illumination as a possible microscopic driving force for enhanced degradation.