Development of a UiO-66 Based Waterborne Flame-Retardant Coating for PC/ABS Material

The flame-retardancy of polymeric materials has garnered great interest. Most of the flame retardants used in copolymers are functionalized additives, which can deteriorate the intrinsic properties of these materials. As a new type of flame retardant, functionalized metal-organic frameworks (MOFs) can be used in surface coatings of polymers. To reduce the flammability, a mixture of phytic acid, multi-wall carbon nanotubes, zirconium-based MOFs, and UiO-66 was coated on a PC/ABS substrate. The structure of the UiO-66-based flame retardant was established by FT-IR, XRD, XPS, and SEM. The flammable properties of coated PC/ABS materials were assessed by LOI, a vertical combustion test, TGA, CCT, and Raman spectroscopy. The presence of a UiO-66-based coating on the PC/ABS surface resulted in a good flame-retardant performance. Heat release and smoke generation were significantly reduced. Importantly, the structure and mechanical properties of PC/ABS were less impacted by the presence of the flame-retardant coating. Hence, this work presents a new strategy for the development of high-performance PC/ABC materials with both excellent flame-retardancy and good mechanical properties.