A sulfur-modified pore-blocking method to enhance the electrocatalytic stability of carbon-supported platinum...

Currently, the durability of electrode materials remains a big obstacle to the widespread adoption of proton exchange membrane fuel cells (PEMFCs). Herein thiourea and sodium dodecyl benzene sulfonate (SDS) were employed as sulfur source and carbon source to modify the pristine carbon black (Ketjen black EC300 J). A highly durable carbon supported Pt nanosized catalyst with higher platinum utilization for oxygen reduction reaction (ORR) in PEMFCs was produced by doping elemental sulfur into carbon supports and decreasing the carbon pore sizes and volume through a successive impregnation technique. The catalyst exhibits an initial activity of 0.167 A mg_Pt ^-1 at 0.90 V and demonstrates minimal activity loss after acceleration stress test (30,000 cycles of AST). The half-wave potential loss for representative sample (Pt/S-C-3) is only 14 mV with only 21.8 % ECSA decrease, 27.5 % MA loss and 5.9 % SA loss. A sintering test at various temperature shows a minor average size increase for sulfur-doped carbon (S-C) supported one (from 2.09 to 2.52 nm). In single-cell test, the MEA sample employing the platinum catalyst on modified carbon as cathode exhibited almost negligible performance loss after 30,000 cycles of AST.