Effect of different surface treatments on shear bond strength of autopolymerizing repair resin to denture base...

To evaluate the effect of chemical, mechanical, and combination surface treatments on the shear bond strength (SBS) of autopolymerizing repair resin to conventional heat-cured, computer aided design (CAD)-computer aided manufacturing (CAM) milled, and three-dimensionally (3D) printed denture base materials.

Specimens were fabricated and divided according to the surface treatment as follows: no surface treatment (control group), monomer treatment (monomer group), resin remover treatment (resin remover group), roughening with 180 FEPA grit abrasive paper followed by monomer treatment (180-grit plus monomer group), and air particle abrasion (air abrasion group). Autopolymerizing resin cylinders were attached before accelerated aging of the specimens in water at 100 °C for 16 h. The SBS was tested using a universal testing machine. Surface roughness was evaluated using a 3D optical profilometer. Scanning electron microscopy (SEM) and stereomicroscopy were used for surface analysis. Data was collected and analyzed using analysis of variance (ANOVA) and Kruskall-Wallis tests (α = 0.05).

The denture base material and surface treatment significantly affected the SBS. The milled Temp Basic Tissue demonstrated the highest SBS values across all surface treatments, whereas the two 3D-printed denture base materials exhibited the lowest SBS values.

The bond strength of CAD-CAM-milled denture base resins to autopolymerizing repair resin is comparable to that of heat-cured resins. Surface roughening using air particle abrasion or 180-grit carbide paper can enhance the bond strength of the autopolymerizing repair resin to 3D-printed denture base materials.