Effect of different production techniques on the color of porcelain-fused-to-titanium restorations

In dentistry, the shade selection of the restoration affects the success of the restoration. For this reason, it may be decisive for clinicians to determine whether the difference in framework production influences color in metal-ceramic restorations. The study examined the effects of different framework production techniques used in porcelain-fused-to-titanium restorations on color changes. 45 square-shaped samples were manufactured using cast, milling, and laser-sintering techniques. Opaque and dentin porcelain were performed, and all samples were glazed. A spectrophotometer was used for color measurements. Before opaque application, after opaque application, and after porcelain + glaze application, it was obtained L*, a*, and b* values. Color differences (ΔE₀₀) were calculated with the CIEDE2000 formula. ANOVA (Post Hoc: Bonferroni) and Shapiro Wilks (Normality) tests were used for statistical analysis (p < 0.05). At the different laboratory steps, the difference between cast&laser-sintered groups and between milled&laser-sintered groups was statistically significant (p < 0.05). Before and after opaque application, the differences in L*, a*, and b* values between cast, milled, and laser-sintered groups were statistically significant (p < 0.05). Different framework production methods influenced the color of porcelain-fused-to-titanium restorations.