Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
Evaluation of the ceramic laminate veneer-tooth interface after different resin cement excess removal techniques
Aline Campos Otani1, Marcos Pascoal Pattussi2, Ana Maria Spohr3
1Post-Graduate Program in Dentistry, School of Health and Life Sciences, Pontifical Catholic University of Rio Grande do Sul (PUCRS), Avenida Ipiranga 6681, Block 6, Porto Alegre, RS, 90619-900, Brazil.
Objectives:
To compare, in vitro, resin cement excess removal techniques at the veneer-tooth interface.
Materials And Methods:
Anterior human teeth were restored with ceramic veneers and randomly divided according to the following techniques (n = 10): removal of excess resin cement with brush and dental floss, followed by light-curing with Valo (Group 1) or Elipar (Group 2) for 1 min and 40 s; tack-curing with Valo (Group 3) or Elipar (Group 4) for 1 s; and tack-curing with Valo (Group 5) or Elipar (Group 6) for 5 s. The tack-curing was followed by removal of excess with probe and dental floss and light-curing for 1 min and 40 s. The area of excess resin cement (mm2) was measured in micro-CT images using AutoCAD program. The failures at the cervical margin in the X, Y, and Z axes (µm) of greater value were measured using the DataViewer program. The specimens were submitted to microleakage with 2% basic fuchsin.
Results:
According to the Kruskal-Wallis and multiple comparison test, the highest area of excess resin cement was found in Group 1 (5.06 mm2), which did not differ statistically from Groups 2 (3.70 mm2) and 5 (2.19 mm2). Groups 2, 3 (1.73 mm2), 4 (1.14 mm2), and 5 (2.18 mm2) did not differ statistically. Group 6 (0.77 mm2) obtained the lowest value, which did not differ statistically from Groups 3 and 4. According to the Kruskal-Wallis and Dunn test, there was no significant difference in failures in X (p = 0.981), Y (p = 0.860), and Z (p = 0.638) axes and no significant difference in microleakage (p = 0.203) among the groups.
Conclusions:
Tack-curing for 1 s or 5 s, followed by removal of excess resin cement using a probe and a dental floss, tended to result in a lower amount of excess material around the margin.
Clinical Relevance:
The technique used for resin cement excess removal influences the amount of excess leaved at the veneer-tooth interface. Tack-curing for 1 s or 5 s is recommended to mitigate the excess resin cement.