Effect of implant type on the stability of cantilever fixed dental prostheses: An in vitro study
Nadja Rohr1,2, Irina Karakas-Stupar2, Sabrina Karlin1
1Biomaterials and Technology, Department of Research, University Center for Dental Medicine Basel UZB, University of Basel, Basel, Switzerland.
Objectives:
To simulate the replacement of a premolar with an implant-supported cantilever fixed dental prosthesis (ICFDP) and how the fracture load is affected by implant type, positioning within the zirconia blank, and aging protocol.
Materials And Methods:
Seventy-two ICFDPs were designed either within the enamel- or dentin layer of a 4Y-PSZ blank for bone-level and tissue-level titanium-zirconium implants. Fracture load was obtained on the cantilever at baseline (no aging) or after aging in a chewing simulator with the load applied within the implant axis (axial aging) or on the cantilever (12 groups with n = 6). A three-way ANOVA was applied (α = .05).
Results:
A three-way ANOVA revealed a significant effect on fracture load values of implant type (p = .006) and aging (p < .001) but not for the position within the zirconia blank (p = .847). Fracture load values significantly increased from baseline bone level (608 ± 118 N) and tissue level (880 ± 293 N) when the implants were aged axially, with higher values for tissue level (1065 ± 182 N) than bone level (797 ± 113 N) (p < .001). However, when the force was applied to the cantilever, fracture load values decreased significantly for tissue-level (493 ± 70 N), while values for bone-level implants remained stable (690 ± 135 N).
Conclusions:
For ICFDPs, the use of bone-level implants is reasonable as catastrophic failures are likely to be restricted to the restoration, whereas with tissue-level implants, the transmucosal portion of the implant is susceptible to deformation, making repair more difficult.