Facile Deficiency Engineering in a Cobalt-Free Perovskite Air Electrode to Achieve Enhanced Performance for Protonic...

As a crucial component responsible for the oxygen reduction reaction (ORR), cobalt-rich perovskite-type cathode materials have been extensively investigated in protonic ceramic fuel cell (PCFC). However, their widespread application at a commercial scale is considerably hindered by the high cost and inadequate stability. In response to these weaknesses, the study presents a novel cobalt-free perovskite oxide, Ba_0.95La_0.05(Fe_0.8Zn_0.2)_0.95O_3-δ (BLFZ0.95), with the triple-conducting (H⁺|O^2-|e^-) property as an active and robust air electrode for PCFC. The B-site deficiency state contributes significantly to the optimization of crystal and electronic structure, as well as the increase in oxygen vacancy concentration, thus in turn favoring the catalytic capacity. As a result, the as-obtained BLFZ0.95 electrode demonstrates exceptional electrochemical performance at 700 °C, representing extremely low area-specific resistance of 0.04 Ω cm² in humid air (3 vol.% H₂O), extraordinarily high peak power density of 1114 mW cm^-2, and improved resistance against CO₂ poisoning. Furthermore, the outstanding long-term durability is achieved without visible deterioration in both symmetrical and single cell modes. This study presents a simple but crucial case for rational design of cobalt-free perovskite cathode materials with appreciable performance via B-site deficiency regulation.