The Crystallization and Melting Behavior of Neodymium-Based Butadiene Rubber Blends

This study investigates the influence of poly(butadiene-isoprene) copolymer rubber (BIR) and TDAE oil on the crystallization and melting behavior of neodymium-based butadiene rubber (Nd-BR). The study demonstrates that the melting points of Nd-BR and its blends decrease with lower crystallization temperatures. Below the critical crystallization temperature (T_c,c), the melting behavior shows dual peaks in distinct temperature ranges, which are attributed to different spherulitic sizes. The addition of BIR or TDAE oil lowers the T_c,c, with TDAE oil exerting a more substantial effect. These diluents mainly influence the nucleation temperature and crystallinity level of Nd-BR while having a minimal effect on the crystallization mechanism. A master curve, which overlaps for various samples, is developed by correlating the peak melting temperature (T_m,peak) with the T_c. This curve facilitates a quantitative assessment of the effects of BIR and TDAE oil on Nd-BR, highlighting the greater influence of TDAE oil on the crystalline structure compared with BIR at equivalent mass fractions. By applying the Lorentz equation and multi-peak fitting, a relationship between the melting points and crystallization temperatures is established, enabling the calculation of the equilibrium melting points (T_m⁰) for different samples. The findings show a reduction in the T_m⁰ due to the diluents; specifically, the T_m⁰ is approximately 0 °C for pure Nd-BR, and it decreases to -4.579 °C and -6.579 °C for samples with 50 PHR TDAE oil and 60 wt.% BIR, respectively.