Effect of Resin-Missing Defects on Tensile Behavior of Carbon Fiber/Epoxy Composites

This study explores the impact of resin-missing defects on the mechanical properties of composite laminates through experimental and finite element methods. Specimens with varying defect contents (5.3%, 8.0%, 10.7%, 13.3%, and 16.7%) were prepared via Vacuum Assistant Resin Infusion process. Experimental tests were conducted with the assistance of Digital Image Correlation measurements to illustrate the impact of resin-missing defects on failure characteristics. The experimental results indicate that the existence of resin-missing defects altered the stress distribution, increased the local stress, and reduced the tensile strength of the composite laminate. The DIC results indicate that the presence of defects weakens the matrix, leading to premature damage and deterioration. Numerical modeling with a progressive damage analysis method was developed to simulate the failure process and the influence of the resin-missing defects. The simulation results agree well with the experimental results, and the maximum error was 3.06%. The failure modes obtained from finite elements are consistent with the experimental and DIC results. Furthermore, a study was conducted on how the location of resin-missing defects affects the mechanical properties of composite laminates. The findings suggest that defects situated at the edges or on the surface of the material have a more significant impact on the tensile strength.