Boosted Electrocatalytic Degradation of Levofloxacin by Chloride Ions: Performances Evaluation and Mechanism Insight...

As chloride (Cl^-) is a commonly found anion in natural water, it has a significant impact on electrocatalytic oxidation processes; yet, the mechanism of radical transformation on different types of anodes remains unexplored. Therefore, this study aims to investigate the influence of chlorine-containing environments on the electrocatalytic degradation performance of levofloxacin using BDD, Ti₄O₇, and Ru-Ti electrodes. The comparative analysis of the electrode performance demonstrated that the presence of Cl^- improved the removal and mineralization efficiency of levofloxacin on all the electrodes. The enhancement was the most pronounced on the Ti₄O₇ electrode and the least significant on the Ru-Ti electrode. The evaluation experiments and EPR characterization revealed that the increased generation of hydroxyl radicals and active chlorine played a major role in the degradation process, particularly on the Ti₄O₇ anode. The electrochemical performance tests indicated that the concentration of Cl^- affected the oxygen evolution potentials of the electrode and consequently influenced the formation of hydroxyl radicals. This study elucidates the mechanism of Cl^- participation in the electrocatalytic degradation of chlorine-containing organic wastewater. Therefore, the highly chlorine-resistant electrocatalytic anode materials hold great potential for the promotion of the practical application of the electrocatalytic treatment of antibiotic wastewater.