Synthesis of soybean soluble polysaccharide-based eco-friendly emulsions for soil erosion prevention and control

This paper introduces the synthesis of an environmentally friendly emulsion that can be used as a soil anti-water erosion material. SSPS-g-P(BA-co-MMA-co-AA) emulsions were prepared using free radical copolymerization with soybean soluble polysaccharide (SSPS), acrylic acid (AA), butyl acrylate (BA), and methyl methacrylate (MMA). The structure, thermal stability, and morphology were characterized using FT-IR,TG,SEM, and particle diameter analysis. The resistance to water erosion, compressive strength and water retention of emulsion-treated loess/laterite was studied and germination tests were conducted. The results demonstrated that the duration of washout resistance of loess with 0.50 wt% emulsion exceeded 99 h, and the water erosion rate was 56.0 % after 72 h, while the water erosion rate of pure loess is 100.0 % after 4 min;the duration of washout resistance of laterite with 0.50 wt% emulsion exceeded 2 h, which was 8 times longer than pure laterite;The compressive strengths of 0.5 wt% emulsion-treated loess/laterite were 3.5 Mpa and 5.8 MPa, respectively, which were 7 and 9 times higher than that of pure soil. The plant seeds germinated normally half a month after planting. These findings suggest that emulsions can be used to control soil erosion without affecting the germination of plant seeds.