Bacteroid cerium oxide particles promote macrophage polarization to achieve early vascularization and subsequent...

The establishment of an osseointegration is crucial for the long-term stability and functionality of implant materials, and early angiogenesis is the key to successful osseointegration. However, the bioinertness of titanium implants affects osseointegration, limiting their clinical application. In this study, inspired by the rapid polarization of macrophages following the phagocytosis of bacteria, we developed bacteroid cerium oxide particles; these particles were composed of CeO₂ and had a size similar to that of Bacillus (0.5 μ m). These particles were constructed on the implant surfaces using a hydrothermal method. In vitro experiments demonstrated that the particles effectively decreased the reactive oxygen species (ROS) levels in macrophages (RAW264.7). Furthermore, these particles exerted effects on M1 macrophage polarization, enhanced nitric oxide (NO) secretion to promote vascular regeneration, and facilitated rapid macrophage transition to the M2 phenotype. Subsequently, the particles facilitated human umbilical vein endothelial cell (HUVEC) migration. In vivo studies showed that these particles rapidly stimulated innate immune responses in animal models, leading to enhanced angiogenesis around the implant and improved osseointegration. In summary, the presence of bacteroid cerium oxide particles on the implant surface regulated and accelerated macrophage polarization, thereby enhancing angiogenesis during the immune response and improving peri-implant osseointegration.