Polymerization efficiency of different bulk-fill resin composites cured by monowave and polywave light-curing units:
Objectives:
The objective was to evaluate the polymerization efficiency of different bulk-fill resin-based composites cured by monowave and polywave light-curing units, by assessment of the degree of conversion and Vickers microhardness at different depths.
Method And Materials:
Two commercially available bulk-fill resin-based composites were used: Filtek One Bulk Fill Restorative (3M ESPE) and Tetric N-Ceram Bulk Fill (Ivoclar Vivadent). The light-curing units utilized were two LED light-curing units: a monowave LED light-curing unit (BlueLEX LD-105, Monitex) and a polywave LED light-curing unit (Twin Wave GT-2000, Monitex). For each test, 20 cylindrical specimens (4 mm diameter, 4 mm thickness) were prepared from each bulk-fill resin-based composite using a split Teflon mold. Ten specimens were light-cured by the monowave light-curing unit and the other ten were light-cured by the polywave light-curing unit according to the manufacturer's recommendations. Attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR) was used to assess the degree of conversion, and a Vickers microhardness tester was used to assess Vickers microhardness. Statistical analysis was performed using three-way ANOVA and Tukey post-hoc tests (P < .05).
Results:
The degree of conversion and Vickers microhardness in bulk-fill resin-based composites containing only camphorquinone as photoinitiator were similar when cured with either monowave or polywave light-curing units. However, bulk-fill resin-based composites containing a combination of photoinitiators exhibited significantly higher degree of conversion and Vickers microhardness when cured with a polywave light-curing unit. Although all groups showed statistically significant differences between the top and bottom surfaces regarding degree of conversion and Vickers microhardness, all of them showed bottom/top ratios > 80% regarding degree of conversion and Vickers microhardness.
Conclusion:
The polywave light-curing unit enhanced the polymerization efficiency of bulk-fill resin-based composites especially when the latter contained a combination of photoinitiators, but does not prevent the use of a monowave light-curing unit.
More Related Videos
09:41Magnet Assisted Composite Manufacturing: A Flexible New Technique for Achieving High Consolidation Pressure in Vacuum Bag/Lay-Up Processes
Published on: May 17, 2018
05:30Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials
Published on: January 10, 2025