Hydrogen adsorption on various transition metal (111) surfaces in water: a DFT forecast

The hydrogen adsorption and hydrogen evolution at the M(111), (M = Ag, Au Cu, Pt, Pd, Ni & Co) surfaces of various transition metals in aqueous suspensions were studied computationally using the DFT methods. The hydrogens are adsorbed dissociatively on all surfaces except on Ag(111) and Au(111) surfaces. The results are validated by reported experimental and computational studies. Hydrogen atoms have large mobility on M(111) surfaces due to the small energy barriers for diffusion on the surface. The hydrogen evolution via the Tafel mechanism is considered at different surface coverage ratios of hydrogen atoms and is used as a descriptor for the hydrogen adsorption capacity on M(111) surfaces. All calculations are performed without considering how the hydrogen atoms are formed on the surface. The hydrogen adsorption energies decrease with the increase in the surface coverage of hydrogen atoms. The surface coverage for the H₂ evolution depends on each M(111) surface. Among the considered M(111) surfaces, Au(111) has the least hydrogen adsorption capacity and Ni, Co and Pd have the highest. Furthermore, experiments proving that after the H₂ evolution reaction (HER) on Au⁰-NPs, and Ag⁰-NPs surfaces some reducing capacity remains on the M⁰-NPs is presented.