Transport of nZVI/copper synthesized by green tea extract in Cr(IV)-contaminated soil: modeling study and reduced...

In this study, nano-zero-valent iron/copper was synthesized by green tea extracts (GT-nZVI/Cu) and produced a stable suspension than nano-zero-valent iron synthesized by green tea extracts (GT-nZVI) injected into Cr(VI)-containing soil column. The equilibrium 1D-CDE model was successfully used to fit the penetration curves of Fe(tot), Fe(aq), and Fe(0) in order to determine the relevant parameters. The hydrodynamic dispersion coefficient of chromium-contaminated soil was 0.401 cm²·h^-1, and the pore flow rate was 0.144 cm·h^-1. The stable C/C₀ of Fe(tot), Fe(aq), and Fe(0) in the effluent were retarded to 0.39, 0.79, and 0.11, respectively, compared to a ratio of 1 for the concentration of the tracer Cl^- in the effluent to the concentration in the influent. Additionally, the 1D-CDE model describes the migration behavior of Cr(VI) with a high R² (> 0.97). The obtained blocking coefficients declined gradually with increasing concentration of GT-nZVI/Cu suspension and decreasing concentration of Cr(VI). The content of reduced chromium in the soil decreased from 2.986 to 1.121 after remediation, while the content of more stable oxidizable chromium and residual chromium increased from 2.975 and 20.021 to 16.471 and 27.612. The phytotoxicity test showed that mung bean seeds still had a germination rate of 90% (control of 100%), root length of 29.63 mm (control of 35.25 mm), and stem length of 17.9 cm (control of 18.96 cm) after remediation with GT-nZVI/Cu. These indicated that GT-nZVI/Cu was effective in immobilizing Cr(VI) in the soil column and reduced the ecological threat. This study provides an analytical basis and theoretical model for the migration of chromium-contaminated soil in practical application.