CdSe nanostructured thin film by electrophoretic deposition for quantum dots sensitized solar cell

Cadmium selenide (CdSe) quantum dots (QDs) with different size, 2.5 and 3.2 nm, were successfully deposited on mesoporous titanium dioxide (TiO₂) (Degussa-P25) nanostructures by electrophoretic deposition method (EPD) at the applied voltage 100 V for 120 s deposition time. In this study, the morphology of CdSe films deposited by EPD and the performance of the film when assembled into a solar cell were investigated. From the field emission scanning electron microscopy cross-section, the thickness of the CdSe nanoparticles with size 2.5 nm films were 3.4 and 3.0μm for CdSe 3.2 nm nanoparticles film. The structure of 2.5 nm is denser than compare of 3.2 nm CdSe nanoparticles. From UV visible spectroscopy, the band gap calculated for 2.5 nm CdSe nanoparticles is 2.28 eV and for 3.2 nm is 2.12 eV. Photovoltaic characterization was performed under an illumination of 100 mW cm^-2. A photovoltaic conversion efficiency of 1.81% was obtained for 2.5 nm CdSe and 2.1% was obtained for 3.2 nm CdSe nanoparticles. This result shows that the photovoltaic efficiency is dependent on CdSe nanoparticle size.