Preparation and Performance Evaluation of Ionic Liquid Copolymer Shale Inhibitor for Drilling Fluid Gel System

An inhibitor that can effectively inhibit shale hydration is necessary for the safe and efficient development of shale gas. In this study, a novel ionic liquid copolymer shale inhibitor (PIL) was prepared by polymerizing the ionic liquid monomers 1-vinyl-3-aminopropylimidazolium bromide, acrylamide, and methacryloyloxyethyl trimethyl ammonium chloride. The chemical structure was characterized using fourier transform infrared spectroscopy (FT-IR) and hydrogen-nuclear magnetic resonance (H-NMR), and the inhibition performance was evaluated using the inhibition of slurrying test, bentonite flocculation test, linear expansion test, and rolling recovery test. The experimental results showed that bentonite had a linear expansion of 27.9% in 1 wt% PIL solution, 18% lower than that in the polyether amine inhibitor. The recovery rate of shale in 1 wt% PIL was 87.4%. The ionic liquid copolymer could work synergistically with the filtrate reducer, reducing filtration loss to 7.2 mL with the addition of 1%. Mechanism analysis showed that PIL adsorbed negatively charged clay particles through cationic groups, which reduced the electrostatic repulsion between particles. Thus, the stability of the bentonite gel systems was destroyed, and the hydration dispersion and expansion of bentonite were inhibited. PIL formed a hydrophobic film on the surface of clay and prevented water from entering into the interlayer of clay. In addition, PIL lowered the surface tension of water, which prevented the water from intruding into the rock under the action of capillary force. These are also the reasons for the superior suppression performance of PIL.