The Effect of Impact Load on the Atomistic Scale Fracture Behavior of Nanocrystalline bcc Iron

Nanocrystalline metals have many applications in nanodevices, especially nanoscale electronics in aerospace. Their ability to resist fracture under impact produced by environmental stress is the main concern of nanodevice design. By carrying out molecular dynamics simulations under different fast loading rates, this work examines the effect of impact load on the fracture behavior of nanocrystalline bcc iron at an atomistic scale. The results show that a crack propagates with intergranular decohesion in nanocrystalline iron. With the increase in impact load, intergranular decohesion weakens, and plastic behaviors are generated by grain boundary activities. Also, the mechanism dominating plastic deformation changes from the atomic slip at the crack tip to obvious grain boundary activities. The grain boundary activities produced by the increase in impact load lead to an increase in the threshold energy for crack cleavage and enhance nanocrystalline bcc iron resistance to fracture. Nanocrystalline bcc iron can keep a high fracture ductility under a large impact load.