Effects of Nd: YAG LASER irradiation and O2 plasma on the adhesive performance of poly-ether-ether-ketone (PEEK)
Tianjie Chen1, Shan Xu2, Xueqing Chen3
1Hospital of Stomatology, Jilin University, Changchun 130012, China; Section of Implant and Rehabilitative Dentistry, Division of Oral Rehabilitation, Faculty of Dental Science, Kyushu University, Fukuoka 812-8582, Japan.
Purpose:
To evaluate the effects of neodymium-doped yttrium aluminum garnet (Nd: YAG) LASER irradiation and oxygen (O2) plasma on the adhesive performance of polyether ether ketone (PEEK) and resin adhesive.
Methods:
Nd: YAG LASERs of varying powers and O2 plasma for different durations were used to modify PEEK. A total of 168 PEEK specimens were randomly divided into seven groups (n = 24/group): (A) Control group: untreated PEEK, (B) L0.75 group: PEEK modified with 0.75 W Nd: YAG LASER, (C) L1 group: PEEK modified with 1.0 W Nd: YAG LASER, (D) L1.25 group: PEEK modified with 1.25 W Nd: YAG LASER, (E) P15 group: PEEK modified with 15 min of O2 plasma, (F) P25 group: PEEK modified with 25 min of O2 plasma, and (G) P35 group: PEEK modified with 35 min of O2 plasma. The surface characteristics of the materials were comprehensively analyzed using a scanning electron microscope (SEM), profilometer, energy-dispersive spectrometer (EDS), and contact angle tester. The adhesive specimens were bonded with Variolink N resin adhesive in all groups and each group was further divided into two subgroups (n = 12/group): (a) water storage for 56 h at 37 °C and (b) thermal cycling 5000 times. Shear bond strength (SBS) was tested using a universal testing machine, and the fracture modes were observed using an automated chemiluminescence analysis system to assess the effects of Nd: YAG LASER and O2 plasma on the bond strength of PEEK to resin adhesive.
Results:
Both Nd: YAG LASER and O2 plasma treatments altered the surface characteristics of PEEK and significantly increased the SBS between PEEK and Variolink N resin adhesive. The L0.75 group (Nd: YAG LASER) and the P35 group (O2 plasma) achieved the highest SBS, respectively. Furthermore, the SBS of the L0.75 group was higher than that of the P35 group. Following thermal cycling, SBS values decreased compared to the water storage subgroups. The fracture modes of the specimens in each group were predominantly interfacial and mixed, with no cohesive fractures observed.
Conclusions:
Nd: YAG LASER irradiation and O2 plasma treatments can improve the SBS between PEEK and resin adhesive, with the 0.75 W Nd: YAG LASER being the preferred treatment method.