Comparison of subcritical growth parameters of a Y-TZP obtained via cyclic or dynamic fatigue tests

The objective of this study was to 1) compare the stress corrosion coefficient (n) of a Y-TZP obtained by two fatigue tests: cyclic and dynamic and 2) evaluate the effect of frequency in the characteristic lifetime and the existence of interaction between the cyclic fatigue and slow crack growth.

A total of 145 Y-TZP specimens were produced in accordance with the manufacturer's instructions. These specimens, measuring 4.0 × 3.0 × 25.0 mm, were used for dynamic (n = 70) and cyclic fatigue tests (n = 75). The specimens were obtained from CAD/CAM blocks, sectioned, and sintered in a furnace at 1530 °C with a heating rate of 25 °C/min. They were tested in their "as-sintered" form without any additional surface treatment. The fatigue tests were conducted using a four-point bending to obtain the slow crack growth parameters (n). The cyclic fatigue test was also conducted in two frequencies (2 and 10 Hz), using stress levels between 350 and 600 MPa. Data from these tests were analyzed using ASTM C 1368-00 formulas and Weibull statistics. Scanning electron microscope (SEM) was used for fracture surface analysis to identify the origin of the fracture. Critical defect size was measured and used, along with flexural strength values, to estimate fracture toughness. Dynamic fatigue test data were used to obtain subcritical crack growth (SCG) parameters and perform Weibull statistical analysis. The cyclic fatigue data were used in the General Log-linear Model equation using the ALTA PRO software. Data were analyzed using one-way ANOVA followed by Tukey post-hoc tests and Student's t-test at a significance level of p ≤ 0.05.

In the dynamic fatigue test, the values obtained for σ_fo and n were 667 and 54, respectively. This parameter indicates how the strength of the material diminishes over time due to internal cracks. The Weibull parameters obtained from the same test results were m = 7.9, σ₀ = 968, 9 and σ_5% = 767, which indicates the reliability of the material. The Weibull parameters obtained by cyclic fatigue were statistically similar for the two frequencies used, the m* was 0.17 (2 Hz) and 0.21 (10 Hz); characteristic lifetimes (η) were 1.93 × 10⁶ and 40,768, respectively. The n values obtained by cyclic fatigue were 48 and 40 at frequencies of 2 and 10 Hz, respectively. There was no effect of the frequency, the stress level or the interaction of the two in the Y-TZP lifetime, when analysed by General Log Linear Model.

the n values obtained by cyclic and dynamic fatigue tests showed no statistically significant difference and the effect of frequency in the characteristic lifetime and the existence of interaction between the cyclic fatigue and subcritical growth were not observed in the tested specimens.