Mechanically Robust and Highly Conductive Poly(ionic liquid)/Polyacrylamide Double-Network Hydrogel Electrolytes for...

Flexible electronic devices, such as supercapacitors (SCs), place high demands on the mechanical properties, ionic conductivity, and electrochemical stability of electrolytes. Hydrogels, which combine flexibility and the advantages of both solid and liquid electrolytes, will meet the demand. Here, we report the synthesis of novel poly(ionic liquid)/polyacrylamide double-network (DN) (PIL/PAM DN) hydrogel electrolytes containing different metal salts via a two-step γ-radiation method. The resultant Li₂SO₄-1.0/PIL/PAM DN hydrogel electrolyte possesses excellent mechanical properties (tensile strength of 3.64 MPa, elongation at break of 446%) and high ionic conductivity (24.1 mS·cm^-1). The corresponding flexible SC based on the Li₂SO₄-1.0/PIL/PAM DN hydrogel electrolyte (SC-Li₂SO₄) presents improved ion diffusion, ideal electrochemical double-layer capacitor behavior, good rate capability, and excellent cyclic stability. Moreover, symmetric SC-Li₂SO₄ achieves a wide operating voltage range of up to 1.5 V, with a maximum energy density of 26.0 W h·kg^-1 and a capacitance retention of 94.1% after 10,000 galvanostatic charge-discharge cycles, owing to the deactivation of free water molecules by the synergistic effect of PIL, PAM, and SO₄^2-. Above all, the capacitance of SC-Li₂SO₄ is well-maintained after overcharge, overdischarge, short circuit, extreme temperature, compression, and bending tests, indicating its high security and flexibility. This work reveals the enormous application potential of PIL-based conductive hydrogel electrolytes for flexible electronic devices.