Green conversion of waste alkaline battery material to zeolitic imidazolate framework-8 and its iodine capture...

Zeolitic imidazolate framework-8 (ZIF-8) exhibits excellent performance in capturing iodine. However, the solvent-based procedures and raw materials for ZIF-8 synthesis often lead to secondary pollution. We developed a solvent-minimizing method for preparing ZIF-8 via ball milling of raw material obtained from spent alkaline batteries, and studied its iodine-capture performance and structural changes. Exposure of the ZIF-8 to iodine vapor for 60 min demonstrated that it exhibited industrially competitive iodine-capture performance (the adsorbed amount reaches to 1123 mg g^-1 within 60 min). Spectroscopic studies showed that ZIF-8 underwent a structural transformation upon iodine loading. Iodine molecules were adsorbed onto the surface of ZIF-8 and also formed C-I bond with the methyl groups on the imidazole rings, reducing iodine release. This work represents a comprehensive revelation of long-range order and short-range order evolution of ZIF-8 during iodine vapor adsorption over time. Moreover, this green synthesis of ZIF-8 is of lower cost and generates fewer harmful by-products than existing methods, and the produced ZIF-8 effectively entraps toxic iodine vapor. Thus, this synthesis enables a sustainable and circular material flow for beneficial utilization of waste materials.