Antibacterial coating of orthodontic elastomeric ligatures with silver and bismuth nanofilms by magnetron
Andrea Schubert1, Carolin Griesmüller1, Nikolaus Gersdorff1
1Department of Prosthodontics, University Medical Center Goettingen, Goettingen, Germany.
Objectives:
Magnetron sputtering was evaluated to equip surfaces of orthodontic elastomeric ligatures with silver and bismuth nanofilms.
Material And Methods:
Antibacterial properties were evaluated by the adhesion of Streptococcus mutans. Polyurethane-based elastomeric ligatures were coated with silver and bismuth nanofilms via direct current magnetron sputtering. Surface roughness (Ra ) and surface-free energy (SFE) were assessed. Coated specimens were incubated with S. mutans for 2 h. Adhering bacteria were visualized by Hoechst staining and quantified by an ATP-based luminescence assay. One-way analysis of variance with Tukey post hoc testing and Pearson correlation analysis were performed (p < .05) to relate bacterial adhesion to surface roughness and surface-free energy.
Results:
Elastomeric ligatures were successfully coated with silver and bismuth nanofilms. Ra was significantly reduced by silver coating. Silver and bismuth coatings showed significantly higher SFE than controls. Adhesion of S. mutans was significantly decreased by silver coating. No correlation between bacterial adhesion and SFE was found. Correlation between bacterial adhesion and Ra was positive but not statistically significant.
Conclusions:
Magnetron sputtering proved to be a feasible method to equip orthodontic elastomeric ligatures with silver and bismuth nanofilms. Silver coatings of elastomeric ligatures may reduce white spots and carious lesions in orthodontic patients. Future research is required to stabilize coatings.