Fluoride-amorphous calcium phosphate and biomimetic nano-hydroxyapatite for enamel remineralization: An in-vitro
Sameh Hamed1, Mohammad H Abd El Latief1, Noha A El-Wassefy2
1Department of Orthodontics, Faculty of Dentistry, Mansoura University, 35516 Mansoura, Egypt.
Aim:
Fluoride-Amorphous Calcium Phosphate and Biomimetic Nano-Hydroxyapatite for Enamel Remineralization; An In-Vitro Study of Surface Microhardness and Composition.
Material And Methods:
Ninety-six extracted human premolars with sound buccal surface were divided using a randomization computer-generating software into four groups; Group I (control) sound untreated enamel, Group II (demineralized) demineralized to create white spot lesions, Group III (biom-n-HA) demineralized and then treated with biomimetic nanohydroxyapatite cream, and Group IV (F-ACP) demineralized and then treated using Fluoride-Amorphous Calcium Phosphate varnish. Each group was divided into two subgroups; subgroup "A" evaluated for mineral content using energy dispersive x-ray spectroscopy (EDX) and for surface microhardness using the Vickers microhardness test and Subgroup "B" evaluated for white spot lesion depth using a polarized light microscope (PLM).
Results:
The highest microhardness (VHN) was found in the (F-ACP) group (mean=428.61±54.43) and then in the (Biom-n-HA) group (mean=408.11±70.16) followed by the (Control) group (mean=402.13±53.40) with no significant difference between them and finally in the significantly different (Demineralized) group (mean=256.99±45.83). The weight percentage of Ca (30.29±1.04 and 33.44±1.07) and Ca/P ratio (1.87±0.06 and 2.03±0.05) were significantly different between Group III and Group IV respectively. PLM measurements in Group II (198.83μm), Group III (60.17μm), and Group IV (26.33μm) were significantly different.
Conclusions:
Both the (Biom-n-HA) cream and the (F-ACP) varnish showed promising results for enamel remineralization. The increased enamel surface microhardness was consistent with the mineral content and the changes in the birefringence.
Related Concept Videos
01:31Essential Minerals for Bone Health
Calcium and Phosphorus
Calcium is a critical component of bones, especially in the form of calcium phosphate and calcium carbonate. Since the body cannot make calcium, it must be obtained from the diet. However, calcium cannot be absorbed from the small intestine without...
01:18The Bone Matrix
01:21Tooth Anatomy
The Crown, Neck, and Root
The visible part of the tooth is referred to as the crown. It's covered by enamel, the hardest substance in the human body. The crown is uniquely shaped for each type of tooth, allowing for different functions such as cutting, tearing, or...