Lightweight, Flexible, and Thermal Insulating Carbon/SiO2@CNTs Composite Aerogel for High-Efficiency Microwave
Xiaohan Wang1,2, Ye Yuan1,2,3, Xianxian Sun1,2,3
1School of Materials Science and Engineering, Beihang University, Beijing, 100191, P. R. China.
Abstract:
A complex electromagnetic environment is a formidable challenge in national defense areas. Microwave-absorbing materials are considered as a strategy to tackle this challenge. In this work, lightweight, flexible, and thermal insulating Carbon/SiO2@CNTs (CSC) aerogel is successfully prepared coupled with outstanding microwave absorbing performance, through freeze-drying and high-temperature annealing techniques. The CSC aerogel shows a strong reflection loss (-55.16 dB) as well as wide effective absorbing bandwidth (8.5 GHz) in 2-18 GHz. It also retains good microwave absorption properties under tension and compression. Radar cross-sectional (RCS) simulation result demonstrates the CSC processing a strong reduction ability of RCS compared with a metal plate. Further exploration shows amazing flexibility and good thermal insulation properties of CSC. The successful preparation of this composite aerogel provides a broad prospect for the design of microwave-absorbing materials.